bluemesa159 Posted November 20, 2008 Share #26 Posted November 20, 2008 Hello...Just a question... How did you manage to get this item in the US???? I want to ship a WWI 1917 Enfield rifle and bayonet ( RELIC CONDITION) from Europe to a forum member, His greathfather was in the 91st Division and this item has been recovered on HILL 263 near Exermont in the Argonne region The 181st Brigade ( 91St USID) came in support to the 1st DIUS in the vicinity of Montrefagne Hill ( HILL240) I am very scared that, once I have shipped the item it will be witheld at the US customs and that both of us will therefore be in trouble, Teufelhund http://www.hqusareur.army.mil/OPM/guns.htm This may not be exactly the information for you, but it's a good starting point. This page is designed for US military in Germany. Where it will help the individual is the ATF (Alcohol, Tobacco & Firearms) forms. Link to comment Share on other sites More sharing options...
Simon Lerenfort Posted November 20, 2008 Share #27 Posted November 20, 2008 A nice find and great to have something that you can relate to your Fathers unit. Link to comment Share on other sites More sharing options...
LtRGFRANK Posted November 20, 2008 Share #28 Posted November 20, 2008 http://www.hqusareur.army.mil/OPM/guns.htmThis may not be exactly the information for you, but it's a good starting point. This page is designed for US military in Germany. Where it will help the individual is the ATF (Alcohol, Tobacco & Firearms) forms. I concure. My son shipped several firearms to me by USPS from Germany. Need the ATF papers and custom papers and there were no problems. This was after 911 and during Clinton Gun Ban Link to comment Share on other sites More sharing options...
jgawne Posted November 20, 2008 Share #29 Posted November 20, 2008 Couple of things- 1. if you do go down to metal with electolysis, you really should coat the result with something like microcrystaline wax which will protect it against further damage, and should someday some amazing product become available you can remove it. Often an item looks a lot better after being waxed, sometimes not. try it on something you do not care about first, and then on a small lesser seen area. 2. I brought a rusted M1 home from France. I packed it in a checked bag as best as possible to cushion it. I did not say anything to anyone about it as it was a rusted peice of metal (one of many I have brought home) and it did not fall into any catagory of declarible items that I could see. If you looked at it on an e-ray I am not sure you would be able to tell what it was. Anyway no one said anything at all. I also had a friend bring a rusted WW1 enfield home. He told the US customs guy that he had a WW2 rifle in his bag, but that it had been in the ground for 75 years and was just a hunk of rust. The customs guy waved him through. 3. evapo rust, and there is something else new and really (really expensive) in the conservation field that is similar. I've found them to be OK, but $$$ and they get crudded up really fast so it ends up being far more expensiv that you planned. Link to comment Share on other sites More sharing options...
Bluehawk Posted November 20, 2008 Share #30 Posted November 20, 2008 Excellent advice ^ - microcrystalline wax is, by far, THE best metal preservative. If all else fails, that wax can be found here: http://www.usmilitariaforum.com/forums/ind...showtopic=26375 Link to comment Share on other sites More sharing options...
SDC Posted November 26, 2008 Author Share #31 Posted November 26, 2008 To answer a few questions; no, electrolysis will not harm stainless steel. An eventual remaining black finish on the gas tube would be removed. Here is a VERY good link wich explains the electrolysis process. http://www.htpaa.org.au/article-electro.php do not use salt in the solution, the bubbles in this solution create hydrogen & oxigen gasses, but also chloric gasses, wich are of course harmfull for humans. Better to use baking soda for the solution. if you use soda, first heat up the water to ease solving the soda. Using a stainless steel tank is the cleanest way, but this creates chromates in the solution, wich are harmful too. Better to use a suitable plastic container, and use rebar as anode. Jon has a point too, you like the result, or you dont. thats a personal preferance. Thats why I try to avoid the process whenever possible. IMO there is nothing wrong with the rust finish, as long as its not a thick crud. Regards, Stijn Stijn: Thank you for this article, it's convinced me to give it a try. One last question though - is there any particular ratio of anode (i.e. rebar) size to the size of the object. More simply, how big a piece of rebar should I use for this M1? Thanks gain, I'll post some pictures of the finished product in a few days. Link to comment Share on other sites More sharing options...
Peace Posted November 26, 2008 Share #32 Posted November 26, 2008 You can use any metal you have, as long as its clean healthy metal to begin with. The cleaner it is, the better the conduction in the water. Keep in mind the metal will degrade fairly quickly, so dont expect to reuse it for something else. I suggest using a few pieces of rebar of maybe a pinky finger thick. Link to comment Share on other sites More sharing options...
Recommended Posts
Create an account or sign in to comment
You need to be a member in order to leave a comment
Create an account
Sign up for a new account in our community. It's easy!
Register a new accountSign in
Already have an account? Sign in here.
Sign In Now